Structural stability, elemental ordering, and transport properties of layered ScTaN2

Fuente: arXiv
Saved in:
Bibliographic Details
Main Authors: Julien, Baptiste, Leahy, Ian A., Smaha, Rebecca W., Mangum, John S., Perkins, Craig L., Bauers, Sage R., Zakutayev, Andriy
Format: Preprint
Published: 2025
Subjects:
Online Access:
Tags: Add Tag
No Tags, Be the first to tag this record!
_version_ 1866918086694666240
author Julien, Baptiste
Leahy, Ian A.
Smaha, Rebecca W.
Mangum, John S.
Perkins, Craig L.
Bauers, Sage R.
Zakutayev, Andriy
author_facet Julien, Baptiste
Leahy, Ian A.
Smaha, Rebecca W.
Mangum, John S.
Perkins, Craig L.
Bauers, Sage R.
Zakutayev, Andriy
contents Some ternary TM nitrides are predicted to adopt layered structures that make them interesting for thermoelectric conversion and quantum materials applications. Synthesis of TM ternary nitride films by physical vapor deposition often favors disordered 3D structures rather than the predicted 2D-like layered structure. In this study, we investigate the structural interplay in the Sc-Ta-N material system, focusing on ScTaN2. We use a two-step combinatorial approach to deposit Sc-Ta-N films by RF co-sputtering and then process the resulting 3D-structured precursor with RTA. Synchrotron GIWAXS on films annealed at 1200 °C for 20 min reveals the nucleation of the layered structure (P63/mmc) within a composition window of x = Sc/(Sc+Ta) = 0.2-0.5. We estimate the long-range order parameter in stoichiometric ScTaN2 films to be 0.86, corresponding to a fraction of antisites of 7%. Interestingly, we find that the structure can accommodate large off-stoichiometry in the Ta-rich region (x < 0.5), facilitated by making an alloy with the nearly isostructural Ta5N6 compound that exists on a composition tie-line. Transport measurements on ScTaN2 reveal a nearly temperature-independent high carrier density (1021 cm-3), suggesting a heavily doped semiconductor or semimetallic character. The carrier mobility is relatively small (9.5 cm2V-1s-1 at 2 K) and the residual-resistivity ratio is small, suggesting that electrical conduction is dominated by defects or disorder. Measured magnetoresistance is indicative of weak antilocalization at low temperatures. We highlight the interplay between ScTaN2 and Ta5N6 in stabilizing layered structures, emphasizes the importance of cation order/disorder for potential tunable alloys, and suggests that ScTaN2 is promising platform for exploring electronic properties in a tie line of stoichiometry.
format Preprint
id arxiv_https___arxiv_org_abs_2503_22857
institution arXiv
publishDate 2025
record_format arxiv
spellingShingle Structural stability, elemental ordering, and transport properties of layered ScTaN2
Julien, Baptiste
Leahy, Ian A.
Smaha, Rebecca W.
Mangum, John S.
Perkins, Craig L.
Bauers, Sage R.
Zakutayev, Andriy
Materials Science
Some ternary TM nitrides are predicted to adopt layered structures that make them interesting for thermoelectric conversion and quantum materials applications. Synthesis of TM ternary nitride films by physical vapor deposition often favors disordered 3D structures rather than the predicted 2D-like layered structure. In this study, we investigate the structural interplay in the Sc-Ta-N material system, focusing on ScTaN2. We use a two-step combinatorial approach to deposit Sc-Ta-N films by RF co-sputtering and then process the resulting 3D-structured precursor with RTA. Synchrotron GIWAXS on films annealed at 1200 °C for 20 min reveals the nucleation of the layered structure (P63/mmc) within a composition window of x = Sc/(Sc+Ta) = 0.2-0.5. We estimate the long-range order parameter in stoichiometric ScTaN2 films to be 0.86, corresponding to a fraction of antisites of 7%. Interestingly, we find that the structure can accommodate large off-stoichiometry in the Ta-rich region (x < 0.5), facilitated by making an alloy with the nearly isostructural Ta5N6 compound that exists on a composition tie-line. Transport measurements on ScTaN2 reveal a nearly temperature-independent high carrier density (1021 cm-3), suggesting a heavily doped semiconductor or semimetallic character. The carrier mobility is relatively small (9.5 cm2V-1s-1 at 2 K) and the residual-resistivity ratio is small, suggesting that electrical conduction is dominated by defects or disorder. Measured magnetoresistance is indicative of weak antilocalization at low temperatures. We highlight the interplay between ScTaN2 and Ta5N6 in stabilizing layered structures, emphasizes the importance of cation order/disorder for potential tunable alloys, and suggests that ScTaN2 is promising platform for exploring electronic properties in a tie line of stoichiometry.
title Structural stability, elemental ordering, and transport properties of layered ScTaN2
topic Materials Science
url https://arxiv.org/abs/2503.22857