Topological passivation makes high strength alloys insensitive to hydrogen embrittlement
Fuente:
arXiv
Saved in:
| Main Authors: | , , , , , , , , |
|---|---|
| Format: | Preprint |
| Published: |
2025
|
| Subjects: | |
| Online Access: | |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| _version_ | 1866912737777418240 |
|---|---|
| author | Cheng, Huijie Sun, Binhan Zhang, Aochen Ponge, Dirk Yan, Fengkai Lu, Tiwen Zhang, Xian-Cheng Raabe, Dierk Tu, Shan-Tung |
| author_facet | Cheng, Huijie Sun, Binhan Zhang, Aochen Ponge, Dirk Yan, Fengkai Lu, Tiwen Zhang, Xian-Cheng Raabe, Dierk Tu, Shan-Tung |
| contents | Infrastructure parts for a hydrogen (H) economy need alloys that are mechanically strong and at the same time resistant to the most dangerous and abrupt type of failure mode, namely, H embrittlement. These two properties are in fundamental conflict, as increasing strength typically amplifies susceptibility to H-related failure. Here, we introduce a new approach to make alloys resistant to H embrittlement, by creating a topological passivation layer (up to a few hundred micrometers thick) near the material surface, the region that is most vulnerable to H ingress and attack. It features instead a layer of ultrafine laminated grains with tens of times higher dislocation density than conventional materials, altering H diffusion, trapping and crack evolution. We tested the concept on a face-centered cubic (FCC) CoCrNi medium entropy model alloy which undergoes severe H-induced intergranular cracking. Two key mechanisms create the topological passivation: First, the high density (up to ~1.3e15 m-2) of H-trapping dislocations within the passivating grain layer decelerates H migration by up to about an order of magnitude, delaying H-induced crack initiation at grain boundaries. More importantly, once unavoidable micro-sized H-induced intergranular cracks emerge in the topmost surface region, they become completely arrested by the laminated grains, due to a transition in the embrittlement mechanism from H-enhanced grain boundary decohesion to highly energy-dissipative dislocation-associated cracking. These effects almost completely eliminate H embrittlement, at even doubled yield strength, when exposing the so architected material to harsh H attack. Our approach leverages surface mechanical treatments to tailor metallic microstructures in surface regions most susceptible to H attack, providing a scalable solution to protect alloys from H-induced damage. |
| format | Preprint |
| id |
arxiv_https___arxiv_org_abs_2512_00131 |
| institution | arXiv |
| publishDate | 2025 |
| record_format | arxiv |
| spellingShingle | Topological passivation makes high strength alloys insensitive to hydrogen embrittlement Cheng, Huijie Sun, Binhan Zhang, Aochen Ponge, Dirk Yan, Fengkai Lu, Tiwen Zhang, Xian-Cheng Raabe, Dierk Tu, Shan-Tung Materials Science Infrastructure parts for a hydrogen (H) economy need alloys that are mechanically strong and at the same time resistant to the most dangerous and abrupt type of failure mode, namely, H embrittlement. These two properties are in fundamental conflict, as increasing strength typically amplifies susceptibility to H-related failure. Here, we introduce a new approach to make alloys resistant to H embrittlement, by creating a topological passivation layer (up to a few hundred micrometers thick) near the material surface, the region that is most vulnerable to H ingress and attack. It features instead a layer of ultrafine laminated grains with tens of times higher dislocation density than conventional materials, altering H diffusion, trapping and crack evolution. We tested the concept on a face-centered cubic (FCC) CoCrNi medium entropy model alloy which undergoes severe H-induced intergranular cracking. Two key mechanisms create the topological passivation: First, the high density (up to ~1.3e15 m-2) of H-trapping dislocations within the passivating grain layer decelerates H migration by up to about an order of magnitude, delaying H-induced crack initiation at grain boundaries. More importantly, once unavoidable micro-sized H-induced intergranular cracks emerge in the topmost surface region, they become completely arrested by the laminated grains, due to a transition in the embrittlement mechanism from H-enhanced grain boundary decohesion to highly energy-dissipative dislocation-associated cracking. These effects almost completely eliminate H embrittlement, at even doubled yield strength, when exposing the so architected material to harsh H attack. Our approach leverages surface mechanical treatments to tailor metallic microstructures in surface regions most susceptible to H attack, providing a scalable solution to protect alloys from H-induced damage. |
| title | Topological passivation makes high strength alloys insensitive to hydrogen embrittlement |
| topic | Materials Science |
| url | https://arxiv.org/abs/2512.00131 |