Anisotropic implantation damage build-up and crystal recovery in $β$-Ga$_2$O$_3$
Fuente:
arXiv
Saved in:
| Main Authors: | , , , , |
|---|---|
| Format: | Preprint |
| Published: |
2026
|
| Subjects: | |
| Online Access: | |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| _version_ | 1866909038837497856 |
|---|---|
| author | Esteves, Duarte Magalhães Magalhães, Sérgio da Costa, Ângelo Rafael Granadeiro Lorenz, Katharina Peres, Marco |
| author_facet | Esteves, Duarte Magalhães Magalhães, Sérgio da Costa, Ângelo Rafael Granadeiro Lorenz, Katharina Peres, Marco |
| contents | The present work aims at investigating the defect accumulation and recovery dynamics in the inherently anisotropic $β$-Ga$_2$O$_3$ lattice. A systematic Rutherford Backscattering Spectrometry in Channelling mode (RBS/C) analysis of Cr-implanted samples was performed across multiple surface orientations and channelling directions. Distinct apparent defect accumulation and annealing rates were observed along different channelling axes, mainly attributed to the shadowing of certain types of defects along some directions. The efficient defect removal observed after annealing was correlated with the strain relaxation observed via High-Resolution X-ray diffraction (HRXRD) at temperatures as low as 500 °C, which is attributed to the removal of point defects. Annealing at higher temperature further improves crystalline quality but at a slower rate. In short, this work enhances the understanding of the effect of structural anisotropic properties of $β$-Ga$_2$O$_3$ during ion implantation, as well as the crystal recovery during thermal annealing, highlighting the interplay between crystallography and defect dynamics. |
| format | Preprint |
| id |
arxiv_https___arxiv_org_abs_2603_08534 |
| institution | arXiv |
| publishDate | 2026 |
| record_format | arxiv |
| spellingShingle | Anisotropic implantation damage build-up and crystal recovery in $β$-Ga$_2$O$_3$ Esteves, Duarte Magalhães Magalhães, Sérgio da Costa, Ângelo Rafael Granadeiro Lorenz, Katharina Peres, Marco Materials Science The present work aims at investigating the defect accumulation and recovery dynamics in the inherently anisotropic $β$-Ga$_2$O$_3$ lattice. A systematic Rutherford Backscattering Spectrometry in Channelling mode (RBS/C) analysis of Cr-implanted samples was performed across multiple surface orientations and channelling directions. Distinct apparent defect accumulation and annealing rates were observed along different channelling axes, mainly attributed to the shadowing of certain types of defects along some directions. The efficient defect removal observed after annealing was correlated with the strain relaxation observed via High-Resolution X-ray diffraction (HRXRD) at temperatures as low as 500 °C, which is attributed to the removal of point defects. Annealing at higher temperature further improves crystalline quality but at a slower rate. In short, this work enhances the understanding of the effect of structural anisotropic properties of $β$-Ga$_2$O$_3$ during ion implantation, as well as the crystal recovery during thermal annealing, highlighting the interplay between crystallography and defect dynamics. |
| title | Anisotropic implantation damage build-up and crystal recovery in $β$-Ga$_2$O$_3$ |
| topic | Materials Science |
| url | https://arxiv.org/abs/2603.08534 |