Evidence of Micron-Scale Ion Damage in (010), (110), and (011) $β-Ga_2O_3$ Epitaxial Layers
Fuente:
arXiv
Salvato in:
| Autori principali: | , , , , |
|---|---|
| Natura: | Preprint |
| Pubblicazione: |
2026
|
| Soggetti: | |
| Accesso online: | |
| Tags: |
Aggiungi Tag
Nessun Tag, puoi essere il primo ad aggiungerne!!
|
| _version_ | 1866910168915116032 |
|---|---|
| author | Peterson, Carl Saha, Chinmoy Nath Liu, Yizheng Speck, James S. Krishnamoorthy, Sriram |
| author_facet | Peterson, Carl Saha, Chinmoy Nath Liu, Yizheng Speck, James S. Krishnamoorthy, Sriram |
| contents | We report on the experimental observation of up to 11.5 $μm$ deep charge depletion in (010), (110), and (011) $β-Ga_2O_3$ epitaxial layers due to ion damage from sputtering and inductively coupled plasma (ICP) etching processes whereas charge depletion in (001) $β-Ga_2O_3$ epitaxial layers was minimal. The orientation-dependent reduction in CV-measured charge density was first observed in $NiO_x$ reactively sputtered heterojunction p-n diodes (HJDs). When compared to reference low-damage Schottky barrier diodes (SBDs), the sputtered HJDs showed a $9.4{\times}$ increase in the specific on resistance $(R_{on,sp})$ and 85% reduction in net donor concentration $(N_D - N_A)$ at zero bias for sputter-damaged HJDs on (010) epitaxial layers whereas HJDs on (001) remained unchanged. Similarly, sputtered SiO2 caused a reduction of $N_D - N_A$ 11.5 $μm$ deep into the (010) material. Next, SBDs were fabricated on $β-Ga_2O_3$ surfaces previously etched via a BCl3 based ICP process and compared to SBDs on un-etched surfaces. The (010) SBDs on etched surfaces exhibited a $7.7{\times}$ increase in $R_{on,sp}$ and a 91% reduction in $N_D - N_A$ at zero bias where the (001) etched diodes exhibited little change. Additionally, (110) and (011) diodes fabricated on ICP damaged surfaces also saw a ~82% reduction in $N_D - N_A$ at zero bias, indicating (110) and (011) are also susceptible to ion damage. Damage in the (010), (110), and (011) diodes is potentially caused by energetic ions that travel into the open channels present along the [010] direction and create compensating point defects which could potentially diffuse further. |
| format | Preprint |
| id |
arxiv_https___arxiv_org_abs_2604_24190 |
| institution | arXiv |
| publishDate | 2026 |
| record_format | arxiv |
| spellingShingle | Evidence of Micron-Scale Ion Damage in (010), (110), and (011) $β-Ga_2O_3$ Epitaxial Layers Peterson, Carl Saha, Chinmoy Nath Liu, Yizheng Speck, James S. Krishnamoorthy, Sriram Applied Physics Materials Science We report on the experimental observation of up to 11.5 $μm$ deep charge depletion in (010), (110), and (011) $β-Ga_2O_3$ epitaxial layers due to ion damage from sputtering and inductively coupled plasma (ICP) etching processes whereas charge depletion in (001) $β-Ga_2O_3$ epitaxial layers was minimal. The orientation-dependent reduction in CV-measured charge density was first observed in $NiO_x$ reactively sputtered heterojunction p-n diodes (HJDs). When compared to reference low-damage Schottky barrier diodes (SBDs), the sputtered HJDs showed a $9.4{\times}$ increase in the specific on resistance $(R_{on,sp})$ and 85% reduction in net donor concentration $(N_D - N_A)$ at zero bias for sputter-damaged HJDs on (010) epitaxial layers whereas HJDs on (001) remained unchanged. Similarly, sputtered SiO2 caused a reduction of $N_D - N_A$ 11.5 $μm$ deep into the (010) material. Next, SBDs were fabricated on $β-Ga_2O_3$ surfaces previously etched via a BCl3 based ICP process and compared to SBDs on un-etched surfaces. The (010) SBDs on etched surfaces exhibited a $7.7{\times}$ increase in $R_{on,sp}$ and a 91% reduction in $N_D - N_A$ at zero bias where the (001) etched diodes exhibited little change. Additionally, (110) and (011) diodes fabricated on ICP damaged surfaces also saw a ~82% reduction in $N_D - N_A$ at zero bias, indicating (110) and (011) are also susceptible to ion damage. Damage in the (010), (110), and (011) diodes is potentially caused by energetic ions that travel into the open channels present along the [010] direction and create compensating point defects which could potentially diffuse further. |
| title | Evidence of Micron-Scale Ion Damage in (010), (110), and (011) $β-Ga_2O_3$ Epitaxial Layers |
| topic | Applied Physics Materials Science |
| url | https://arxiv.org/abs/2604.24190 |