Tabla de Contenidos:
- Electron Beam-Induced Deposition (EBID) enables site-specific nanofabrication but suffers from significant carbon contamination, limiting its applicability in plasmonics, nanoelectronics, and sensing. In this study, we investigate the relationship between EBID process parameters such as beam current, acceleration voltage, and dwell time, and the platinum-to-carbon composition of deposited nanostructures. Using Energy Dispersive X-Ray Spectroscopy (EDX), we establish a hindered exponential growth model that correlates deposit composition with fabrication conditions. To enhance metal purity, we apply plasma oxygen treatment, exposing EBID deposits to a 30 W plasma for 30 minutes in a tabletop plasma generator. Post-treatment EDX analysis confirms a systematic increase in platinum content, while SEM inspection reveals nanostructure shrinkage due to carbon removal. This work aims to provide a framework for optimizing EBID fabrication and post-processing strategies to enhance material performance.