Sol-gel synthesis of zinc oxide nanoparticle at three different temperatures and its characterization via XRD, IR and EPR
Fuente:
Redalyc
Saved in:
| Main Author: | |
|---|---|
| Format: | Artículo científico |
| Language: | en |
| Published: |
Universidad Nacional de Colombia
2016
|
| Subjects: | |
| Online Access: | |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| _version_ | 1876474539888607232 |
|---|---|
| author | Manuel Acosta-Humánez |
| author_facet | Manuel Acosta-Humánez |
| contents | Sol-gel synthesis of zinc oxide nanoparticle at three different temperatures and its characterization via XRD, IR and EPR Manuel Acosta-Humánez Luis Montes-Vides Ovidio Almanza-Montero Ingeniería sol gel method zinc oxide Ray diffraction IR spectroscopy In this work, nanoparticles of zinc oxide were synthesized; they were formed using the sol-gel method (citrate route) at calcination temperatures (Tc) of 500, 550 and 600 °C. For all samples studied, IR spectroscopy showed the presence of the bands associated with water molecules present in the zinc oxide and carbon dioxide adsorbed on its surface. The formation of zinc oxide phase was confirmed by XRD, which showed that from 500 ºC it had this type of Wurtzite structure. However, samples calcinated at 600 ºC have higher crystallinity. Crystallite size was calculated using the Scherrer equation. The Rietveld method was used to obtain lattice parameters a and c for Wurtzite cell types as well as cell volume and the ratio c/a of each sample. These parameters do not show significant changes when they are compared with values obtained from samples with different calcination temperatures. Electron paramagnetic resonance showed the presence of defects in the zinc oxide. Three signals with g values of 1.96, 2.00 and 2.04 were associated with oxygen and zinc vacancies. Defects in the structure disappear when the calcination temperature is increased. The sample that was highlighted with the highest concentration of vacancies has a mean crystallite size greater than 30 nm, and this may also be responsible for this feature. 2016 artículo científico 0012-7353 https://www.redalyc.org/articulo.oa?id=49644128028 en http://www.redalyc.org/revista.oa?id=496 Dyna application/pdf Universidad Nacional de Colombia Dyna (Colombia) Num.195 Vol.83 |
| format | Artículo científico |
| id | redalyc_49644128028 |
| institution | Redalyc |
| language | en |
| publishDate | 2016 |
| publisher | Universidad Nacional de Colombia |
| spellingShingle | Sol-gel synthesis of zinc oxide nanoparticle at three different temperatures and its characterization via XRD, IR and EPR Manuel Acosta-Humánez Ingeniería sol gel method zinc oxide Ray diffraction IR spectroscopy Sol-gel synthesis of zinc oxide nanoparticle at three different temperatures and its characterization via XRD, IR and EPR Manuel Acosta-Humánez Luis Montes-Vides Ovidio Almanza-Montero Ingeniería sol gel method zinc oxide Ray diffraction IR spectroscopy In this work, nanoparticles of zinc oxide were synthesized; they were formed using the sol-gel method (citrate route) at calcination temperatures (Tc) of 500, 550 and 600 °C. For all samples studied, IR spectroscopy showed the presence of the bands associated with water molecules present in the zinc oxide and carbon dioxide adsorbed on its surface. The formation of zinc oxide phase was confirmed by XRD, which showed that from 500 ºC it had this type of Wurtzite structure. However, samples calcinated at 600 ºC have higher crystallinity. Crystallite size was calculated using the Scherrer equation. The Rietveld method was used to obtain lattice parameters a and c for Wurtzite cell types as well as cell volume and the ratio c/a of each sample. These parameters do not show significant changes when they are compared with values obtained from samples with different calcination temperatures. Electron paramagnetic resonance showed the presence of defects in the zinc oxide. Three signals with g values of 1.96, 2.00 and 2.04 were associated with oxygen and zinc vacancies. Defects in the structure disappear when the calcination temperature is increased. The sample that was highlighted with the highest concentration of vacancies has a mean crystallite size greater than 30 nm, and this may also be responsible for this feature. 2016 artículo científico 0012-7353 https://www.redalyc.org/articulo.oa?id=49644128028 en http://www.redalyc.org/revista.oa?id=496 Dyna application/pdf Universidad Nacional de Colombia Dyna (Colombia) Num.195 Vol.83 |
| title | Sol-gel synthesis of zinc oxide nanoparticle at three different temperatures and its characterization via XRD, IR and EPR |
| topic | Ingeniería sol gel method zinc oxide Ray diffraction IR spectroscopy |
| url | https://www.redalyc.org/articulo.oa?id=49644128028 |