Effects of the calcination temperature and the load of sodium carboxymethyl cellulose in the synthesis of novel bentonite ceramic foams
Fuente:
Redalyc
Enregistré dans:
| Auteur principal: | |
|---|---|
| Format: | Artículo científico |
| Langue: | en |
| Publié: |
Universidad Libre
2017
|
| Sujets: | |
| Accès en ligne: | |
| Tags: |
Ajouter un tag
Pas de tags, Soyez le premier à ajouter un tag!
|
| _version_ | 1876422689532411904 |
|---|---|
| author | D. Torres |
| author_facet | D. Torres |
| contents | Effects of the calcination temperature and the load of sodium carboxymethyl cellulose in the synthesis of novel bentonite ceramic foams D. Torres J. Villarroel-Rocha K. Sapag A. Gutarra Ingeniería bentonite Ceramic foams replication process calcination temperature sodium carboxymethyl cellulose Novel ceramic foams were obtained by the replica method, using bentonite as alternative raw material and polyurethane sponge as template, where the latter also controls the distribution of the pore size of these ceramics. The synthesis of the ceramics was carried out using slurries of bentonite clay with different percentages of sodium carboxymethyl cellulose as a binder, and evaluating different calcination temperatures. The effect of these factors on the textural and morphological properties of the ceramic foams was studied. The porosity measured by mercury intrusion showed that the total porosity of the ceramic foams decreases as the calcination temperature increases. Furthermore, a small quantity of porosity is generated after the burnout of the binder during the calcination step. This porosity is given by pore sizes from 0.05 to 3 μm and it was increased with the amount of the binder that was increased, which was also confirmed by scanning electron micrographs. The characterization of bentonite clay, polyurethane, coated polyurethane sponge and ceramic foams was also complemented with thermogravimetric analysis, nitrogen adsorption at 77 K, and mechanical strength measurements. 2017 artículo científico 2619-6581 https://www.redalyc.org/articulo.oa?id=757979601009 en http://www.redalyc.org/revista.oa?id=7579 Avances application/pdf Universidad Libre Avances (Colombia) Num.1 Vol.14 |
| format | Artículo científico |
| id | redalyc_757979601009 |
| institution | Redalyc |
| language | en |
| publishDate | 2017 |
| publisher | Universidad Libre |
| spellingShingle | Effects of the calcination temperature and the load of sodium carboxymethyl cellulose in the synthesis of novel bentonite ceramic foams D. Torres Ingeniería bentonite Ceramic foams replication process calcination temperature sodium carboxymethyl cellulose Effects of the calcination temperature and the load of sodium carboxymethyl cellulose in the synthesis of novel bentonite ceramic foams D. Torres J. Villarroel-Rocha K. Sapag A. Gutarra Ingeniería bentonite Ceramic foams replication process calcination temperature sodium carboxymethyl cellulose Novel ceramic foams were obtained by the replica method, using bentonite as alternative raw material and polyurethane sponge as template, where the latter also controls the distribution of the pore size of these ceramics. The synthesis of the ceramics was carried out using slurries of bentonite clay with different percentages of sodium carboxymethyl cellulose as a binder, and evaluating different calcination temperatures. The effect of these factors on the textural and morphological properties of the ceramic foams was studied. The porosity measured by mercury intrusion showed that the total porosity of the ceramic foams decreases as the calcination temperature increases. Furthermore, a small quantity of porosity is generated after the burnout of the binder during the calcination step. This porosity is given by pore sizes from 0.05 to 3 μm and it was increased with the amount of the binder that was increased, which was also confirmed by scanning electron micrographs. The characterization of bentonite clay, polyurethane, coated polyurethane sponge and ceramic foams was also complemented with thermogravimetric analysis, nitrogen adsorption at 77 K, and mechanical strength measurements. 2017 artículo científico 2619-6581 https://www.redalyc.org/articulo.oa?id=757979601009 en http://www.redalyc.org/revista.oa?id=7579 Avances application/pdf Universidad Libre Avances (Colombia) Num.1 Vol.14 |
| title | Effects of the calcination temperature and the load of sodium carboxymethyl cellulose in the synthesis of novel bentonite ceramic foams |
| topic | Ingeniería bentonite Ceramic foams replication process calcination temperature sodium carboxymethyl cellulose |
| url | https://www.redalyc.org/articulo.oa?id=757979601009 |