Corrosion Failure Analysis of 316L Stainless Steel Exposed to the China's Bohai Sea Water‐Air Interfacial Environment for 2.5 years

Fuente: Wiley Open Access

Guardado en:

Detalles Bibliográficos
Autores principales:	Futai Zhang, Mingyu Wang, Wanbin Chen, Yunze Xu, Bernard Tribollet, Zhenbo Qin, Da‐Hai Xia
Formato:	Artículo Open Access
Publicado:	Wiley 2026
Materias:	Materials and Corrosion
Acceso en línea:	Acceder al recurso
Etiquetas:	Agregar Etiqueta Sin Etiquetas, Sea el primero en etiquetar este registro!

Ejemplares similares

Effect of Mg Content on the Mechanical and Corrosion Behavior of AlSi10Mg x Alloys via Selective Laser Melting
por: Chengcheng Pan, et al.
Publicado: (2025)

Effect of Surface Mechanical Rolling Treatment on the Corrosion Behavior of 316L Stainless Steel
por: Taoran Sun, et al.
Publicado: (2025)

Empirical Study of the Effect of Nanocoolant Particles on Corrosion Rate of 316 Stainless Steel
por: Yuli Panca Asmara, et al.
Publicado: (2024)

Experimental and Comparative Study of the Corrosion Behavior of Lean Duplex Stainless Steel in Seawater
por: Mohammad Hassanzadeh, et al.
Publicado: (2026)

Human Blood Investigation of Ta‐Coated 316L Stainless Steel to Evaluate Corrosion and Wear Behaviour Against Other Artificial Fluids for Orthopaedic Implants
por: Dileep Pathote, et al.
Publicado: (2025)

Corrosion Behavior of Two Kinds of Stainless Steels in a Novel Ternary Nitrate/Nitrite Molten Salt
por: Jinli Li, et al.
Publicado: (2025)

Effect of Oxygen and Nitrogen Oxide Gas Concentration on Corrosion of 310N Stainless Steel in Solar Salt at 600°C
por: Sumit Kumar, et al.
Publicado: (2026)

Optimize the Corrosion and Mechanical Performance of Additive‐Manufactured Nano‐Size WC‐Reinforced Stainless Steel Matrix Composites by Heat Treatments
por: Yiqi Zhou, et al.
Publicado: (2024)

Reinforcement Corrosion Rate and Crack Width Relationship in Concrete Beams Exposed to Simulated Marine Environment
por: Y. Hernández
Publicado: (2016)

Effect of Heat Treatment Parameters on Microstructure, Hardness, and Corrosion Resistance of Martensitic Stainless Steel X30Cr13 (AISI 420B)
por: Adrian Evia Ocampo, et al.
Publicado: (2026)

Corrosion Mechanism and Simulation of Q235 Steel in Typical Marine Atmospheric Environment
por: Shuo Cai, et al.
Publicado: (2025)

Exploring Galvanic Corrosion Behavior of CFRP/Q235 Carbon Steel in Marine Environment
por: Yue Hou, et al.
Publicado: (2025)

Corrosion Cracking of 316L Steel Under Fatigue Loading in High‐Temperature Binary Nitrate Salt: Effects of Loading Frequency
por: Deming Wang, et al.
Publicado: (2025)

Investigation and In Vitro Studies of a ZrO2/g‐C3N4 Composite Coated on 316L Stainless Steel for Biomedical Applications
por: Manoja Tharmaraj, et al.
Publicado: (2024)

Study of Atmospheric Corrosion of Reinforcement Steel in Havana, Cuba.
por: Abel Castañeda
Publicado: (2014)

Passivation of Prestressed Steel in Concrete With Slag and Exposed to Chlorides
por: Sreelakshmi Srinivasan, et al.
Publicado: (2025)

Effect of Temperature and Oxygen Concentration on Corrosion of J55 Steel in an O2/CO2 Environment
por: Haozhe Ma, et al.
Publicado: (2024)

Nonlinear Corrosion Evolution and Lateral Bearing Capacity Degradation of Steel Tubular Piles Under Marine Environment
por: Wei Shao, et al.
Publicado: (2025)

Microbiological Characterization of Natural Seawater Collected on the Brazilian Atlantic Coast—Impact on Carbon Steel Corrosion
por: Carolina Paz Garín Correa, et al.
Publicado: (2025)

Corrosion Performance of Prepainted Galvanized Steel After 8‐Year Outdoor Exposure Upon the Distance to the Seashore in Temperate Environment
por: Nathalie LeBozec, et al.
Publicado: (2026)

Kurtosis as a Decisive Topographic Parameter for Pitting Attack of AISI 304L Stainless Steel
por: Alireza Kalhor, et al.
Publicado: (2025)

Propagation of Corrosion‐Induced Cracking of the Reinforced Concrete Exposed to Stray Current in Rail Infrastructures
por: Wenjun Zhu, et al.
Publicado: (2025)

Performance of Surface‐Engineered SAE 4140 Valve Stem Steel Under High‐Temperature Cyclic Oxidation and Hot‐Corrosion Environment
por: Pravin Kumar Mishra, et al.
Publicado: (2026)

Microbially Influenced Corrosion in Epoxy‐Ceramic Coated Carbon‐Steel Cooler
por: Veronika Hlavackova, et al.
Publicado: (2025)

Optimizing the Resistance of Advanced Weathering Steel to Marine Atmospheric Corrosion With the Addition of Al
por: Yitong Yan, et al.
Publicado: (2025)

Effect of Drying on the Corrosion of Carbon Steel, Zinc, Aluminium and AZ31B Magnesium Alloy During Cyclic Accelerated Corrosion Tests
por: Kateryna Popova, et al.
Publicado: (2025)

Sol‐Gel Coating on CA‐60 Steel Surfaces: A Process for Corrosion Inhibition
por: Aguinaldo Manoel da Silva Junior, et al.
Publicado: (2025)

Evaluation of the Surface Treatment Utilizing KH570 on 304 Stainless Steel Tower Packing: The Effect of Silanization to Modify Tower Packing
por: Gao Sheng Wu, et al.
Publicado: (2026)

Top‐ and Bottom‐of‐the‐Line Corrosion (TLC and BLC): Effects of 30°C Bottom Liquid and 12°C Steel Temperature in H 2 S and CO 2 Environments
por: Muhammad Taqiuddin, et al.
Publicado: (2026)

Beneficial Effect of Grain Refinement on the Oxidation Resistance of T91 Steel Exposed to Liquid Lead–Bismuth Eutectic
por: Zhiwei Ma, et al.
Publicado: (2025)

Corrosion Behavior and Evaluation Method of Pipeline Steel Under Dynamic AC Interference: A Study
por: Le Chen, et al.
Publicado: (2024)

Hybrid Ceramic–Industrial Waste Reinforced HVOF Coatings for Erosion–Corrosion Protection of Boiler Steels
por: Duraisammy Elango, et al.
Publicado: (2025)

The Effect of NO 2 on the Corrosion Mechanism of P110 Tubing Steel Used for CO 2 Storage
por: Zhen Yang, et al.
Publicado: (2025)

MOF‐5@Phen@Chitosan/EP Coating: A Smart Dual‐Functionality Self‐Reporting and Corrosion‐Inhibiting Coating for Identifying and Suppressing Early Steel Corrosion
por: Botao Zhao, et al.
Publicado: (2026)

Ant‐Nest Corrosion Morphology of Deoxidized High Phosphorous Copper and Oxygen‐Free Copper Tubes Exposed to Formic Acid Vapor
por: Eri Akisawa, et al.
Publicado: (2025)

Stress Corrosion Tests for Prestressing Steels—Part 2: Susceptibility of Quenched and Tempered Wires—Influence of Chromium
por: Lando Seifert, et al.
Publicado: (2025)

Combined Influence of Microorganisms and Direct Current on the Corrosion Behavior of X70 Steel in Near‐Neutral Solution
por: Yuhan Wang, et al.
Publicado: (2025)

The Inhibitory Properties of the Ambroxol Derivative on the Corrosion of Mild Steel in Hydrochloric Acid Medium
por: Pavel Anatolyevich Nikolaychuk, et al.
Publicado: (2024)

Cover Picture: Materials and Corrosion. 4/2024
por: Jinqing Liang, et al.
Publicado: (2024)

Effect of Minor Cerium Addition on the Oxidation Behavior of Silicon in Ferritic/Martensitic Steel Exposed to Lead‐Bismuth Eutectic at 500°C
por: Hanbing Jia, et al.
Publicado: (2025)