Influence of pulse duration on the fatigue behavior of a carbon‐fiber‐reinforced composite under cyclic three‐point bending at 20 kHz

Documenti analoghi

• Comparability of Fatigue Strength and Life Estimation of a CF‐PEKK Composite Under Low and Ultrasonic Frequencies Using Time‐Temperature‐Based Approaches
  di: Aravind Premanand, et al.
  Pubblicazione: (2025)
• Very high cycle fatigue of fiber‐reinforced polymer composites: Uniaxial ultrasonic fatigue
  di: Alireza Behvar, et al.
  Pubblicazione: (2024)
• Experimental investigations on the fatigue behavior of hybrid basalt/glass fiber epoxy composites
  di: Mayank Agrawal, et al.
  Pubblicazione: (2024)
• Micromechanical modeling of longitudinal compression behavior and failure mechanism of unidirectional carbon fiber reinforced aluminum composites involving initial fiber misalignment
  di: Wengang Jiang, et al.
  Pubblicazione: (2024)
• In situ observation of fatigue crack propagation in soda‐lime glass with initial crack and residual stress induced by Vickers indentation under four‐point bending
  di: Hibiki Komine, et al.
  Pubblicazione: (2024)