Fatigue life prediction of additively manufactured AlSi10Mg based on surface roughness and residual stress

Documenti analoghi

• Fatigue Behavior and Life Prediction of Additively Manufactured AlSi10Mg up to 108 Cycles Under Rotating Bending
  di: Zhonghua Jiang, et al.
  Pubblicazione: (2025)
• Predicting the Size‐Dependent Fatigue Strength Distributions in Additively Manufactured AlSi10Mg Alloy Specimens Using Extreme Value Statistics
  di: Tomasz Tomaszewski, et al.
  Pubblicazione: (2026)
• Multicale Study of the Fatigue Life of AlSi10Mg Material Produced by Laser Powder Bed Fusion (LPBF) Method: Experimental and Computational
  di: Kiarash Jamali Dogahe, et al.
  Pubblicazione: (2025)
• Effect of corrosion pit on fatigue damage and failure in powder bed fusion AlSi10Mg
  di: Haipeng Song, et al.
  Pubblicazione: (2024)
• Fatigue Assessment of Precorroded AlSi9Cu3 Specimens Incorporating Short Crack Propagation
  di: Peter Oberreiter, et al.
  Pubblicazione: (2025)