Atomic Mechanisms and Mechanical Enhancement of Supersonic Fine Particle Bombarding‐Induced Microcrack Healing in γ‐TiAl

Fuente: Wiley Open Access

Guardado en:

Detalles Bibliográficos
Autores principales:	Hui Cao, Ziqi Lu, Xingyou Ding, Wenke Chen, Ruicheng Feng
Formato:	Artículo Open Access
Publicado:	Wiley 2026
Materias:	Fatigue & Fracture of Engineering Materials & Structures
Acceso en línea:	Acceder al recurso
Etiquetas:	Agregar Etiqueta Sin Etiquetas, Sea el primero en etiquetar este registro!

Ejemplares similares

Fatigue Performances of Additively Manufactured γ‐TiAl and IN939 Alloys in As‐Built and Laser Shock–Peened Conditions
por: Mahmut Ozer, et al.
Publicado: (2025)

Stress‐Dependent Microcrack Evolution and Damage Constitutive Model of Low Permeability Sandstone
por: Ming Tang, et al.
Publicado: (2025)

Microscale Investigation on the Monotonic Tension and Fatigue Deformation‐Failure Mechanisms of TiC/Ti6Al4V Composites
por: Zifan Hu, et al.
Publicado: (2025)

Discrete Element Simulation on Mechanical Behavior and Fracture Evolution Mechanism of Regular Joint Rock Under Triaxial Compression
por: Yi‐Ling Hua, et al.
Publicado: (2025)

Mechanism of Fatigue Failure Anisotropy of Extruded Al‐Cu‐Li Alloy
por: Jianwei Yang, et al.
Publicado: (2025)

Dynamic Tensile Mechanical Properties and Fracture Mechanism of Sandstone Exposed to Chemical Corrosion
por: Ben He, et al.
Publicado: (2025)

The Thermal Fatigue Acceleration Test Method, Damage Mechanism, and Life Prediction Model of Diesel Engine Al‐Si Alloy Piston
por: Peiyou Xiong, et al.
Publicado: (2025)

Influence of Notch Geometry and Temperature on the Mechanical Properties of Al‐Mg Alloy Using Molecular Dynamics Simulations
por: Francesco Gucci, et al.
Publicado: (2025)

Resistance of fatigue crack propagation induced by large α colony in a Ti‐Al‐V‐Mo‐Zr alloy
por: Yikui Liu, et al.
Publicado: (2024)

Dynamic Amorphization and Potential Recovery Mechanisms in Silicon Carbide Fatigue: Atomic‐Scale Insights Across Single‐Crystal to Polycrystalline Structures
por: Qingfeng Zeng, et al.
Publicado: (2026)

Fracture Toughness of Ti‐6Al‐4V and Ti‐6Al‐4V ELI Alloys Fabricated by Electron Beam Melting With Different Orientation and Positions
por: Rubén Niñerola, et al.
Publicado: (2025)

Evaluation of Fretting‐Induced Degradation in Steel Wire Rope Strand Using Continuum Damage Mechanics
por: Sajjad Ahmad, et al.
Publicado: (2025)

Defect Healing Mechanism in Fe‐Cr‐Ni Single Crystal Alloy Under Multiaxial Cyclic Loading: A Molecular Dynamics Simulation‐Based Study
por: Arun Kumar, et al.
Publicado: (2025)

Transition Mechanisms of Very‐High Cycle Fatigue Failure in High‐Strength Al Alloy: Effects of Processing States on S‐N Behavior
por: Zepeng Liu, et al.
Publicado: (2025)

Influence of Aging Treatment on the Fatigue Behavior and Fracture Mechanism of SiCp/Al Composites Under Multiaxial Proportional and Non‐Proportional Loadings
por: Yinfu Liu, et al.
Publicado: (2025)

Damage Proportion Analysis of the Combined High and Low Cycle Fatigue Based on the Continuum Damage Mechanics
por: Xin Ding, et al.
Publicado: (2024)

Additively manufactured Ti‐6Al‐4V microstructure tailoring for improved fatigue life performance
por: Roger Beal, et al.
Publicado: (2024)

The Mechanical Behaviors of Sandstones in Response to True Triaxial Graded Perturbations of the Intermediate Principal Stress
por: Junchao Chen, et al.
Publicado: (2025)

An Investigation on Fatigue Strengthening Mechanism of 316L Stainless Steel Welded Joint by Surface Mechanical Rolling Treatment
por: Weiya Jin, et al.
Publicado: (2025)

Fracture Characteristics and Bolting‐Induced Strength Enhancement and Crack Suppression Effect of Jointed Rock
por: Hanxiang Liu, et al.
Publicado: (2025)

Size Effect of High‐Cycle Fatigue Performance in Additively Manufactured Ti‐6Al‐4V Alloy
por: Yining Zhang, et al.
Publicado: (2025)

Investigation of Fretting Fatigue Behavior of Shot Peening–Treated Ti‐6Al‐4V Dovetail Joints
por: Zhiguo Wang, et al.
Publicado: (2025)

Fatigue Crack Nucleation and Growth in Recrystallized Annealed Ti‐6Al‐4V Combat Aircraft Structures
por: I. Field, et al.
Publicado: (2026)

Assessment of the Effect of Multiscale Geometrical Discontinuities on Fatigue Performance of Additively Manufactured Ti6Al4V
por: Susong Yang, et al.
Publicado: (2025)

Evolution of Mechanical Behaviors, Consolidation and Failure Mechanisms in Sandstone Materials Under Compressive Stress: The Role of Chemical Remediation Cycles
por: Jun Li, et al.
Publicado: (2026)

Fatigue Behavior and Fracture Mechanism of 310S Austenitic Stainless Steel Processed by Surface Mechanical Rolling Treatment at 650°C
por: Y. G. Wang, et al.
Publicado: (2025)

Investigation of Fatigue Mechanics and Crack Evolution Characteristics of Jointed Specimens Under Cyclic Uniaxial Compression
por: Miao Chen, et al.
Publicado: (2024)

Effect of Weak‐Filled Layer Properties on the Mechanical Response, Crack Evolution, and Failure Characteristics of Jointed Rock
por: Bowen Xue, et al.
Publicado: (2026)

Analysis of Fatigue Crack Propagation With Multiple Mechanisms
por: Daniel Kujawski
Publicado: (2026)

Fatigue Life Prediction of Powertrain Rubber Suspension Bushings Based on Multiple Damage Parameters Under Thermo‐Mechanical Coupling
por: Hui Wang, et al.
Publicado: (2025)

Crystal plasticity modeling fatigue behavior in bimodal Ti–6Al–4V: Effects of microdefect and lamellar orientation
por: Yindun Zhao, et al.
Publicado: (2024)

Strain Field Visualization During Fatigue Crack Growth in Microstructure Tailored LPBF Ti‐6Al‐4V
por: Roger Beal, et al.
Publicado: (2025)

Vibration bending fatigue analysis of Ti‐6Al‐4V airfoil blades repaired using additive manufacturing
por: Lucas Smith, et al.
Publicado: (2024)

Unraveling the Effect of Retained Austenite on the Very High Cycle Fatigue Crack Initiation Mechanism of Carbide‐Free Bainitic Steel
por: Kun Wang, et al.
Publicado: (2025)

On the Relative Significance of Roughness, Printing Defects and Microstructure on the Fatigue Behavior of Electron Beam Melted Ti‐6Al‐4V
por: Marcos Antonio Bergant, et al.
Publicado: (2025)

The effect of residual stress on high‐cycle fatigue properties and its evaluation method of Ti‐6Al‐4V alloy
por: Shuai Chang, et al.
Publicado: (2024)

Effect of intra‐build design parameters on the fracture toughness properties of Electron Beam Melted Ti6Al4V
por: Naghmeh Melody Mojib, et al.
Publicado: (2024)

Effect of chemical etching time on the fatigue behavior of Ti‐6Al‐4V produced by laser powder bed fusion
por: David Melle, et al.
Publicado: (2024)

Fatigue Crack Segmentation and Characterization of Additively Manufactured Ti‐6Al‐4V Using X‐Ray Computed Tomography
por: Bardia Hejazi, et al.
Publicado: (2024)

High‐ and Very High‐Cycle Fatigue Behaviors and Crack Initiation Mechanism of Alloy 718 at 650°C
por: Yong‐Jie Wang, et al.
Publicado: (2026)