Initial damage behavior of Al 2 O 3 ‐modified SiC f /SiC–B 4 C composites after oxidation under wet atmosphere at 1200°C

Documenti analoghi

• Corrosion behavior of precracked SiC f /SiC composites under 1200–1300°C Na 2 SO 4 ‐wet‐oxygen environment
  di: Feiyu Guo, et al.
  Pubblicazione: (2024)
• Oxidation behaviors of yttrium silicate modified SiC f /SiC composites in air and water‐oxygen environments
  di: Fang He, et al.
  Pubblicazione: (2024)
• Gelcasting for the densification repair of delamination defects in SiC f /SiC composites
  di: Yiran Lin, et al.
  Pubblicazione: (2026)
• Preparation and mechanical behavior of Yb 2 Si 2 O 7 interphase in SiC f /SiC minicomposites
  di: Shuang Mu, et al.
  Pubblicazione: (2024)
• Densification and optimization of SiC f /SiC composites by low‐temperature NITE process
  di: Xu Shen, et al.
  Pubblicazione: (2025)